1.0introduction介绍
1.1TESTSCOPE试验范围
Thisstandardspecifiesanacceleratedlaboratoryatmosphericcorrosiontest.Thetestingenvironmentaddressedissimilarineffecttothatofthesaltload/climaticpartoftheprovinggroundcorrosiontestprocedure,CETP00.00-R-343andyieldscorrespondingresults.Theobjectiveofthetestistoallowevaluationofthecorrosionresistanceofmetalsinenvironmentswherethereisasignificantinfluenceofchlorideions,mainlyassodiumchloridefromamarinesourceorbywinterroadde-icingsalt.Thelaboratorytestprovidesfullexposuretothesaltloadandhumidityenvironment.Itdoesnotattempttosimulateotherengravingfactorssuchasmudloads,temperaturestressesorwear.Itservesasageneralpurposeatmosphericcorrosiontestandappliestoavarietyofmaterials,coatings,andinteractionsofmaterials,bothastestspecimensorindesignedcomponents.Thetestcanbeusedasadesignverificationmethodinorderto(a)developandqualifynewcorrosionresistantproducts,(b)developnewpre-treatmentsandfinishingprocesses,(c)selectmaterialsand,(d)performqualitycontrolofthefinalproduct.
本标准是关于一项在实验室里加速进行的大气腐蚀试验。
本文所述的试验环境类似于《试验场腐蚀试验程序CETP00.00-R-343》中的盐负荷/环境影响部分,得出相应的结果。
试验目的在于评估金属在富含氯化物的环境中(主要是海水中的盐或冬天用于融雪的盐)的抗腐蚀性。
该实验室试验主要是将试验件完全暴露在湿润的盐负荷环境中,而非模拟其他摩擦因素如泥负荷、温度压力或磨损。
该试验主要作为一项大气腐蚀试验,适用于各种各样的材料、涂层、试样或设计零部件材料的相互作用。
该试验可作为一种验证设计的方法,用于(a)开发并验证新的抗腐蚀产品;(b)开发新的预处理和表面处理工艺;(c)选择材料;(d)对最终产品的质量控制。
Thestandardspecifiescontrolledconditionsforequipmentandprocedurestoallowthetesttobeperformedwithahighdegreeofrepeatabilityandreproducibility.Itisdesignedtobesuitabletoruninvariousclimatechambers,eitherasafullyautomatedprocedureorwithpartialmanualoperations.
本标准说明了设备和程序的受控条件,让实验具有高度的重复性和再现性。
本标准适用于多种环境试验箱,包括全自动试验或部分手动操作的试验。
1.2SUMMARYOFTESTCONTENT试验内容摘要
Theworkdaytestprocedureconsistsof:
工作日的试验程序由以下几个方面组成:
∙A6hwetphaseatroomtemperature.withintermittentexposuretosaltsolution(0.5%NaCl).
∙A2.5htransitionphasewithdryingunderclimatecontrol.
∙A15.5hphasewithconstanttemperatureandhumidity(50C,70%RH).
∙室温下6小时的加湿阶段,间歇曝露到0.5%的氯化钠溶液中
∙2.5小时的过渡阶段,通过环境控制进行烘干
∙15.5小时的恒温恒湿阶段(50C,70%RH)
AfterrepeatingthisprocedureMon-Fria48hweekendphaseundercontinuedconstantclimatecontrolisadded.
从周一到周五重复该试验程序后,在周末加入持续恒定环境控,进行48小时的试验。
1.3COMMONALITY共通性
ThisisaCONTROLTESTandcanbeusedtoqualifycomponentsthroughouttheworld.Thetestmaybeconductedatanylocationhavingthenecessaryequipmentandfacilities.ProposedrevisionstothisproceduremustbesubmittedperFAP03-179.
这是一项可验证世界上所有的零部件的控制试验,可在任何地方进行,只要具备所需的设备仪器。
对本试验程序的修改建议必须按FAP03-179提交。
2.0Instrumentation仪器
Thefollowingelementsareusuallyrequiredtoconductthetestprocedure:
进行试验程序一般需要以下仪器:
2.1Compressed,cleanairof4-6barsforcleaningsaltsolutionfromspraynozzles,asasourcefortherenewalofchamberairandforhumidification,suppliedbysprayhumidifiers.
2.14-6bar的干净的压缩空气,用于清理喷嘴上的盐溶液、箱内换气和喷雾加湿器进行加湿。
2.2Alowconductivitywatersupply(20Smax)forhumidificationorevaporativesprayhumidifiersandforthepreparationofsaltsolutions.
2.2一根低导电率的供水管(最大20S),用于加湿或喷雾加湿器以及准备盐溶液。
2.3Atankforpreparationandstorageofsaltsolutionor,alternatively,asystemfordirecton-linemixingofwaterandsaturatedNaClsolutiontotheactualconcentration(0.50.05%byweight)
2.3一个用于准备和存储盐溶液的水槽,或者一套直接在线按实际浓度(0.50.05%,按重量)混合水和饱和氯化钠溶液的系统。
2.4Aconductivitymeterwithbuilt-intemperaturecompensationforpreparationandcontrolofthe0.5%NaClsaltsolution(conductivity:
8.3mS/cm+0.80at20C).A0.50%byweightNaClsolutionisusedasacalibrationstandardateachmeasurement.
2.4一个带内置温度补偿的电导仪,用于准备和控制0.5%的氯化钠盐溶液(温度为20C时的导电性:
8.3mS/cm+0.80)。
一份按重量为0.50%的氯化钠溶液,作为每次测量时的校正标准。
2.5Ahighqualitydeviceforindependentcontroloftemperatureandrelativehumidityshallbeaccessible.Thisinstrumentshallonastipulatedregularinterval(Ref5.4)beusedforindependentmonitoringandcalibrationoftheconditionsintheverytestplaneoftheexposurechamber.Thetotalmeasurementerrormustnotexceed0.1C.
2.5一套高质量的设备,用于独立控制温度和相对湿度。
该设备按照规定的时间间隔(参考5.4),独立监控和校正试验箱李的试验平面上的各项条件,测量总误差不超过0.1C。
2.6Racksofinertmaterialforsupportandalignedfixationoftestspecimensmustnothamperafreeair-flowaroundthetestobjects,norcollectstandingwetness.Thetestobjectsinarackmustnotscreenoneanotherfromthesaltsolutiondownfallandtheyshouldbeexposedwiththestipulatedexposureangletothespray(15-20degreesinclinationfromvertical).
2.6由惰性材料制成的夹具,用于支撑、排列和固定试样,但不得妨碍试样周围的空气流通,不得累积水分。
夹具上的试样不得相互遮蔽导致盐溶液淋不到试样上。
试样应按规定的角度曝露到喷雾中(偏离垂直线15-20度)。
2.7Pressurizedhand-sprayequipmentforapplicationofthe0.5%NaClsolutionifamanualsprayprocedureisused.Thecapacitymustbesufficienttomeetthedownfallrequirement(Ref.3.3.1).
2.7如需采取手动喷洒,应使用适用于0.5%盐溶液的加压型手动喷雾器,喷雾器的容量必须能满足喷洒要求(见3.3.1)。
2.8Funnels,beakers/measuringglassesandabalancewithatleast0.1gaccuracyformonitoringandcalibrationofsaltsolutiondownfallthroughoutthetestplaneoftheexposurechamber.
2.8漏斗、烧杯/量杯以及精确度至少为0.1g的天平,用于监控和校准曝露箱中试验平面上落下的盐溶液。
2.9AlltestmeasurementequipmentmustbecalibratedandmaintainedperFAP03-015,Control,Calibration,andMaintenanceofMeasurementandTestEquipment.
2.9所有试验的测量设备的校准和维护必须按照《FAP03-015测量和试验设备的控制,校准和维护程序》。
2.10Allapplicablesafetyguidelinesandproceduresmustbefollowed.
2.10试验须遵守所有适用的安全指引和安全程序。
3.0Equipmentandfacilities设备设施
Thenecessary,permanentlyinstalledfacilitytoconductthetestconsistsofaprogrammablehumiditychamberofgoodquality.Itispreferablyequippedwithanintegratedrigforsprayingsaltsolutionoftherequiredamountandaccuracy,coolingcapacityandagoodinternalcirculationsystemfortheconditionedair(Fig.1).Theexposurechambershallbedesignedsothatthetestconditionsdescribedinthesubsequentparagraphscanbeobtained,controlled,andmonitoredduringthetest.
试验所需的永久性安装的设施包括一个可编程的高质量湿度箱。
湿度箱中最好能配备一套喷量准确度高的综合性盐雾喷洒装置、冷却装置和一套性能良好的空气内循环系统(如图1)。
曝露箱应按要求设计,以使下文所述的试验过程中的各项条件能在得到满足、控制和监控。
Fig.1Schematicviewofaclimatechamberequippedwithfunctionssuitedforperformanceofthedescribedtestprocedure:
1.Chambertestspace,2.Climatizationunit,includingfan,heating,coolingandhumidification,3.Testplanewithsamples,4.Temperature/humiditysensorforregulation,5.Insulatedwalls/lids,6.Diffusorsforimprovedairdistribution,7.Freshairinlet/"bleed",8.Rainrigwithnozzlesandmotorforswayingmode,9.Gutter,10.Control/steering/recordingunit,11.Positionformonitoring/calibrationofclimatewithindependenttemperature/humiditysensor.
图1环境试验箱的图示,配备了进行本文所述的试验程序所需的功能:
1.试验空间;2.环境系统,包括风扇、加热器、冷却器和加湿器;3.放置试样的平面;4.温湿传感器(调节用);5.隔热壁/盖;6.空气扩散器(改善空气分布);7.新鲜空气进气口;8.带喷头和摇摆模式驱动马达的喷洒器;9.排水口;10.控制/操作/记录系统;11.带独立温室感应器的环境监控/校正位置。
3.1CLIMATECONTROL环境控制
Thehumidityandtemperaturelevelsofthechamberduringthetestcycleshallbecontinuouslymonitored.Thesensorsshouldreflecttheclimateconditionsinthetest"plane"(Fig.1,item4).Themeanvalueoftheconstanttemperature/relativehumidityclimateconditionsmustbewithin±0.4Cand2%relativehumidity(RH)respectivelyvs.thereal,setvalue,i.e.thesearethemaxtolerablemeanoffsetscausedbythesumofcalibrationerrors.Atannualcalibrationthisdegreeofaccuracymustbefulfilledforthefollowingthreeconstantconditions:
25C,95%RH,50C,95%RHand50C,70%RH.Atbimonthlycontrol,duringnormaloperation,thisaccuracyshouldbefulfilledattheconstantclimateconditions(50C,70%RH)duringawork-daycycle.
试验过程中应连续不断地监控试验箱的湿度和温度水平。
传感器会反映试验“平面”上的环境(如图1中第4项)。
恒定温度/相对湿度的均值必须在±0.4C范围内,相对湿度(RH)在±2%,分别对应实际值、设定值,这些就是由于累积的校正误差造成的平均偏移值的最大允许范围。
在年度校正过程中,这一精确度必须得到满足,以保证以下三项恒定条件:
25C,95%RH,50C,95%RH以及50C,70%RH。
在进行两月一次的正常控制时,工作日循环中的恒定环境条件(50C,70%RH)应能到达这一精度。
Themaximumallowedshort-termfluctuationsinrelativehumidityoverlaidonthecalibratedmeanvalueis3%RH,whichimpliesamaximumallowedshort-termtemperaturefluctuationof±0.6C.Figure2isexemplifyingtherequirementonrelativehumidity.
叠加到校正平均值的相对湿度短期波动最大范围是3%RH。
这意味着短期温度波动的最大范围只能是±0.6C。
图2举例说明了相对湿度的要求。
ActualmeanRHvalue
相对湿度实际均值
ActualfluctuationaroundmeanRHvalue
相对湿度均值上下的实际波动
Trueness:
Maxallowedabsolutecalibrationerror:
2%RH
真实:
最大允许的校正误差绝对值:
20%RH
Precision:
Maxallowedvariationaroundactualmeanvalue:
3%RH
精确度:
实际均值上下允许的最大变动范围是:
3%RH
SetRHvalue
相对湿度设定值
Fig.2Accuracyrequirementonhumiditydeviationsfromsetvalue
图2湿度偏差离设定值的精确度要求
Thechambercontrollingsoftware/hardwaremustbedesignedsothattherelativehumiditymaybechangedlinearlywithtimeasdepictedintheillustratedtestconditions,seeFigure5.Inthe2-stagerampingfromawetchamberat25±2Ctohumidconditionsat50C,70%RH,thefirstheatingstageto40Cshouldbereachedwithin30minuteswithoutsampledrying,whichissecuredbyanominalrelativehumiditysettingto95%RH.Thesecond2hrampmustreachthestipulatedfinal50C,70%RHattheendoftheramp.
控制试验箱的软件/硬件必须设计成能使相对湿度随时间呈线性变化,如图5所示。
从试验箱温度为25±2C的湿润状态到50C,70%RH的湿润状态需经过两个阶段。
第一阶段应通过将相对湿度读数设定到95%RH,以保证温度在30分钟内达到40C而试样不干燥。
第二阶段为两小时,必须在结束前达到规定的50C,70%RH。
NOTE:
Foreachnewexposuresituationthisconditionmustbeverifiedbyanindependentmonitoringdevice(paragraph2.5)withthesensorpositionedamongtheactualtestobjectsintheiractualaverageplaneofexposure(Fig.1Item11).Formonitoring:
Deploythesensordirectlyafterthelastsprayeventofthework-daywetphase.
注意:
每次曝露的条件必须经过独立监控设备验证(见第2.5段),也就是实际试验物体所在的曝露平面之间的传感器(如图1,第11项)。
在工作日湿润阶段的最后一次喷洒后直接调节传感器来进行监控。
Inautomatedtesting,for
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- CETPL 全球 实验室 加速 循环 腐蚀 试验 DOC