局部焊后热处理程序LOCALPWHTPROCEDURE教学文案
局部焊后热处理程序
LOCALPWHTPROCEDURE
TableofContent
1.PURPOSE......................................................................................................................................................2
2.SCOPE...........................................................................................................................................................2
3.REFERENCES..............................................................................................................................................2
4.METHODOFPWHT...................................................................................................................................2
5.REQUIREMENTS.........................................................................................................................................3
5.1PREPARATIONPRIORTOPWHT..................................................................................................................3
5.2EXECUTIONOFPWHT...............................................................................................................................5
5.3PWHTRECORDSYSTEM...........................................................................................................................5
1.PURPOSE
Duringinstallationsofthe5feedstocktanks,somepartswillbecarriedoutPWHTonsite.ThisprocedureisissuedtoensurethatPWHTcancarryoutsmoothly,andthatparametersandqualityofPWHTcanmeetrequirementsofcontract,andappliedpecification/standardtosatisfytheowner.
目的:
原料油储罐安装过程中,一些部件需进行现场热处理,本程序的发布,是为了保证现场热处理工作的顺利进行,使热处理参数、质量符合合同、适用规范和标准的要求,使业主满意。
2.SCOPE
ThisprocedureisapplicabletolocalPWHTofmanholes,nozzles,andreinforcementplatesof5feedstocktanksofXXXxPetrochemicalProject.Ifmanholesandnozzlesarewithreinforcementplates,andthicknessofplatewhichman-holeandnozzleareinismorethan12mm,PWHTshallbecarriedoutafterman-holes,nozzles,andreinforcementplateshavebeenassembledandweldedwiththeplatewhichtheyshouldbein,andtheyareaccepted.
范围:
本施工程序适用于xx石油化工有限公司原料油罐安装中,对人孔、接管及补强板的热处理施工。
如果人孔、接管带有补强板,并且所在壁板的厚度大于12mm,那么,在补强板及开口接管与相应罐壁板组装焊接并检验合格后,应进行消除应力热处理。
3.REFERENCES
3.1“Verticalcylindricalsteelweldedoiltank”GBJ128-90
3.2“WeldedSteelTanksforOilStorage”API-650
3.3PMCRelevantWeldingProceduresXX-0038
3.4WELDINGOFMETALSXX.18-XX
3.1《立式圆筒形钢制焊接油罐施工及验收规范》GBJ128-90
3.2《钢制焊接油罐》API-650
3.3PMC相关焊接文件XX-0038
3.4金属的焊接XX.18-XX
4.MethodofPWHT
PostWeldHeatTreatment(PWHT)isheattreatmentcarriedoutafterweldingwiththeaimtoreduceresidualstressesandtorestoretoughnesspropertiesafterdegradationbywelding.
ThemethodofPWHTiselectricheating.ThecaterpillarelectricheaterandlinearelectricheatershouldbefixedonthepartsneededtoPWHT,theyconnectwiththeautomaticcontrollerthroughcable.Andthe
thermocoupleshouldbefixedonthepartsneededtoPWHTthroughthecompensatingconductor,itconnectswiththecomputerautomaticcontroller.Thenthecontrollerwillworkautomaticallyaccordingtotheprocessparameterthatisbeinginputtedintothecontroller.
热处理方法
PWHT是焊后进行的热处理,目的是减少残余应力,恢复由于焊接而降低的韧性。
热处理方法采用电加热。
把履带式电加热片、绳状电加热器固定到需热处理部位,通过电缆与自动温控记录设备连接,把热电偶固定到需热处理部位,通过补偿导线与电脑自动温控记录设备连接。
向该设备
输入热处理工艺参数,设备自动按所定热处理工艺参数进行热处理。
5.REQUIREMENTS
5.1PreparationpriortoPWHT
热处理前准备
5.1.1InspectionofweldingseamWeldingseaminPWHTareashouldbeacceptedthroughNDE,reinforcementplateshouldbeacceptedaftertheinspectionofairtightness,andinspectionreportshouldalsobeprepared.
焊缝检查
热处理部位的焊缝应是探伤合格的,补强板是经过气密检查合格的,并有检查报告。
5.1.2Reinforcingofworkpiece
IfDN≥500mm,themanholeandnozzleshouldbereinforcedthroughL100angleirontopreventthedistortionofworkpiece.Asthedrawinglistedbelow,angleironshouldbeweldedontheworkpiece.After
PWHT,angleironshouldberemoved,andPTshouldbedonetothepalacewheretheangleironisremoved.
工件加固对DN≥500mm的人孔、接管,L100用的角钢进行加固,防止工件产生变形。
如下图所示,角钢焊接在工件上。
热处理后,把角钢磨除,磨除处进行PT。
5.1.3FixingofelectricheaterLinearelectricheatermaywraparoundthefilletweldbetweenmanholeandnozzle,thecaterpillarelectricheatershouldbefixedontheshellandthereinforcementplatethroughbarforlineandsteelwire.
Theheatersshouldbelayoutintheinsideandoutsideofthetankshell.
电加热片固定
绳状电加热器可缠绕在人孔、接管与罐壁的角焊缝位置,履带式电加热片用保温钉和钢丝绑扎固
定在罐壁和补强板上,在罐壁内外双面布置。
5.1.4
Thermocoupleattachmentsshouldbe:
-capacitydischargeconnection,or
-nutandboltconstruction(asshownbelow)
Twotackwelds(oppositeeachother)Thermocoupleinsertion
Ifthelattermethodisused,thematerialsshouldbeofacompatiblecomposition.TheweldmetalshallberemovedbycarefuldressingfollowedbyMTorPTexaminationafterPWHTtoconfirmabsenceof
linearindications.
Allthermocoupleattachmentsshallbeadequatelyinsulatedtoavoidtemperaturemisreadingcausedby
theeffectofradiation.
Thenumberandpositionsofthethermocouplesshallbeinaccordancewiththefollowing:
-Forthenozzlefilletweld,onethermocoupleshouldbelayoutoutsideandinsiderespectively,andthetwopositionsshouldbesymmetrical.
-Fortheseamofreinforcementplate,twothermocouplesshouldbelayoutoutsideofshelloppositeeachother.
-Thethermocoupleshouldbeplacedinthedistanceof5—20mmfromthefringeoftheweldingseam.
热电偶固定
热电偶应该采用:
-电容放电连接,或
-螺母螺栓连接(螺母对称点焊两点,插入热电偶)。
如果采用后一种方法,材料应是相配的。
热处理后,焊接金属仔细修磨去掉,进行MT或PT,确保没有线性指示。
所有热电偶应该足够隔热,避免散热引起的温度读数偏差。
热电偶的数量和位置按以下要求:
-对于接管角焊缝位置,在罐壁内外各一点,交错对称布置;
-对于补强板焊缝位置,在罐外侧对称布置两点;
-热电偶在距焊缝边缘外5~20mm处。
5.1.5保温Heatpreservation
Heatpreservationmaterialshouldbealuminasilicatefibrofelt,andthethicknessofheatpreservationshouldbeabout100mm,thefibrofeltsshouldbefixedbyironwireandbarforlineweldedinthetank
shelltemporarily.Thedistanceof800mmfromtheelectricheatingweldingseamshouldbeheatpreserved,thebodiesofmanholeandnozzlealsoshouldbeheatpreserved.
保温材料选用硅酸铝纤维毡,保温厚度100mm,纤维毡利用焊在罐壁上的保温钉绑扎铁丝固定。
热处理焊缝以外800mm内均应保温,人孔、接管本身也应保温。
5.1.6PWHTequipment
PWHTcontrollersandtime-temperaturerecordersshallbeproperlycalibratedandmaintainedingoodworkingorderatalltimes.Therecordersshallbeprocuredwithacalibrationcertificate,andshallbe
re-calibratedatthestatedintervalsinaccordancewiththeContractorsapprovedcalibrationprocedures.
Eachequipmentshouldbeconnectedthroughconductors.
热处理设备
热处理设备包括热电偶、时间—温度记录仪、和控制器。
它们应加以正确校准并保持良好的工作状态。
热电偶、记录仪应具有校准证明书,并且应依据承包商批准的校准程序在规定的时间间隔内重新校准。
各个设备用导线连接好。
5.2ExecutionofPWHT
Afterthepreparationhascompleted,PWHTshouldbecarriedout.Inputtheprocessparameterintothecontrollerandputontheswitch,andthenPWHTbeginstocarryout.
PWHTprocessparameterseesthefollowing:
Heattreatmenttemperature:
600~650℃
Holdingtime:
>160minutes
Heatingspeed:
<150℃/h
Coolingspeed:
<210℃/h
Note:
300℃below,heatingspeedandcoolingspeedshallbenotcontrolled,butshallbenothigh.
热处理实施
当所有热处理前准备工作完成后,可以进行热处理工作。
把热处理工艺参数输入控制器,打开电源开关,热处理工作即开始进行。
热处理工艺参数如下:
热处理温度:
600~650℃
恒温时间:
>160minutes
升温速度:
<150℃/h
降温速度:
<210℃/h
说明:
300℃以下时,升温速度和冷却速度不需控制,但不应太高。
热处理曲线见下图:
5.3PWHTRecordSystem
焊后热处理记录系统
Time-TemperatureCharts(PostWeldHeatTreatmentCharts)andPWHTreportsofeachpostweld
heat-treatingoperationshallbeprovided.Heattreatrecordsshallindicate:
应提供每个焊后热处理操作的时间—温度图(焊后热处理图)和热处理报告。
热处理记录应包括:
●Applicablecode采用的规范
●Identificationofjointsorpieces接头或工件的识别号
●Projectidentification项目识别号
●Dateofpostweldtreatment焊接后热处理日期
●SignatureofPWHTsupervisorandQCWeldingInspector
焊接后热处理主管及质量控制焊接检验员的签名
●Wallthickness壁厚
●Heatingrate加温速率
●Chartspeed记录纸速
●Holdtime保温时间
●Holdtimebegin保温开始时间
●Holdtimeend保温结束时间
●Powerofftime电源断开时间
●Coolingrates冷却速率
5.4NDEafterPWHT
AfterthecompletionofPWHT,MTorPTshouldbedonetoweldingseamintheareaofPWHT,andnocrackisaccepted.
NoweldingorheatingshallbecarriedoutafterfinalPWHT.
热处理后NDE
热处理完成后,对热处理区域内的焊缝进行MT或PT,无裂纹为合格。
热处理完成后,不能再进行焊接和加热。
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- 局部焊后热处理程序LOCAL PWHT PROCEDURE教学文案 局部 热处理 程序 LOCAL PROCEDURE 教学 文案