Fillingphase:
Status:
V=Velocitycontrol
P=Pressurecontrol
V/P=Velocity/pressureswitch-over
|-------------------------------------------------------------|
|Time|Volume|Pressure|Clampforce|Flowrate|Status|
|(s)|(%)|(MPa)|(tonne)|(cm^3/s)||
|0.25|4.20|7.71|4.34|441.92|V|
|0.50|8.87|12.20|16.95|485.10|V|
|0.74|13.48|15.99|38.17|480.56|V|
|0.98|17.98|20.85|79.31|480.06|V|
|1.23|22.65|25.65|134.77|484.03|V|
|1.47|27.23|30.39|202.10|485.47|V|
|1.72|31.81|35.11|282.36|488.61|V|
|1.97|36.58|40.06|381.25|491.44|V|
|2.21|41.22|44.52|483.00|494.45|V|
|2.45|45.83|49.45|611.51|494.44|V|
|2.70|50.57|54.59|765.69|492.31|V|
|2.95|55.15|59.99|937.90|496.41|V|
|3.19|59.67|64.97|1105.54|499.49|V|
|3.43|64.36|70.14|1291.49|500.91|V|
|3.68|69.11|75.35|1494.82|502.35|V|
|3.92|73.66|80.19|1699.99|503.89|V|
|4.17|78.43|85.30|1934.89|505.82|V|
|4.41|83.13|90.23|2184.04|506.97|V|
|4.66|87.74|95.01|2439.39|508.52|V|
|4.91|92.48|100.01|2726.84|509.75|V|
|5.08|95.68||||V/P|
|5.08|95.68|106.06|3112.09|503.26|P|
|5.15|96.54|84.85|2592.91|247.17|P|
|5.40|98.17|84.85|3007.69|156.82|P|
|5.71|98.99|84.85|3399.84|82.69|P|
|5.90|99.38|84.85|3477.54|64.25|P|
|6.14|99.73|84.85|3537.26|49.34|P|
|6.37|99.97|84.85|3585.52|38.73|P|
|6.38|99.98|84.85|3592.73|37.66|P|
|6.39|100.00|84.85|3599.93|37.66|Filled|
图169.充模分析的屏幕输出文件
屏幕输出文件和结果概要都有与图170相似的部分。
它同时包含了分析过程中(第一部分)和分析结束时的关键信息。
使用这些信息可以快速查看这些变量,从而判断是否需要详细分析某一结果,以发现问题。
Fillingphaseresultssummaryforthepart:
Bulktemperature-maximum(at4.906s)=252.5450C
Bulktemperature-95thpercentile(at5.082s)=251.2430C
Bulktemperature-5thpercentile(at6.389s)=214.1860C
Bulktemperature-minimum(at6.379s)=105.0260C
Wallshearstress-maximum(at6.389s)=0.6826MPa
Wallshearstress-95thpercentile(at0.249s)=0.3107MPa
Shearrate-maximum(at4.906s)=4725.27981/s
Shearrate-95thpercentile(at0.249s)=2489.98001/s
Endoffillingphaseresultssummaryforthepart:
Totalpartweight=2512.5301g
Bulktemperature-maximum=247.0680C
Bulktemperature-95thpercentile=244.5620C
Bulktemperature-5thpercentile=214.1860C
Bulktemperature-minimum=105.0370C
Bulktemperature-average=233.7720C
Bulktemperature-RMSdeviation=12.9527C
Wallshearstress-maximum=0.6826MPa
Wallshearstress-95thpercentile=0.1478MPa
Wallshearstress-average=0.0926MPa
Wallshearstress-RMSdeviation=0.0443MPa
Frozenlayerfraction-maximum=0.5465
Frozenlayerfraction-95thpercentile=0.1257
Frozenlayerfraction-5thpercentile=0.0649
Frozenlayerfraction-minimum=0.0000
Frozenlayerfraction-average=0.0898
Frozenlayerfraction-RMSdeviation=0.0263
Shearrate-maximum=2176.53001/s
Shearrate-95thpercentile=58.98571/s
Shearrate-average=22.88841/s
Shearrate-RMSdeviation=27.09471/s
图170.结果概要输出
充模时间(FillTime)
充模时间显示的是熔体流动前沿的扩展情况,其默认绘制方式是阴影图,但使用云纹图
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- MOLDFLOW 分析 结果 解释